Lembaran Tantalum
Komposisi kimia:
| Komponen utama dan kecil | kandungan min(%) | ASTM B386 (361) |
| Ta | 99.95 | imbangan |
| kekotoran | Nilai maks (μg/g) | Nilai maks (μg/g) |
| Fe | 100 | 100 |
| Mo | 100 | 200 |
| Nb | 400 | 100 |
| Ni | 50 | 100 |
| Si | 50 | 50 |
| Ti | 50 | 100 |
| W | 100 | 500 |
| C | 30 | 200 |
| H | 15 | 15 |
| N | 50 | 100 |
| O | 100 | 250 |
| Cd | 10 | - |
| Hg | 10 | - |
| Pb | 10 | - |
Dimensi dan toleransi
| Ketebalan (mm) | Toleransi ketebalan (±mm atau % daripada ketebalan） | Toleransi lebar±mm | |
| Lebar≤320mm | 320mm≤Width≤610mm | ||
| 0.10 | 0.008 | 0.5 | |
| 0.10-0.15 | 0.010 | 0.5 | |
| 0.15-0.30 | 0.010 | 0.5 | |
| 0.30-0.40 | 0.015 | 0.037 | 1.6 |
| 0.40-0.60 | 0.020 | 0.050 | 1.6 |
| 0.60-0.80 | 0.030 | 0.065 | 1.6 |
| 0.80-1.00 | 0.035 | 0.080 | 1.6 |
| 1.00-2.50 | 0.040 | 0.100 | 2.0 |
| 2.50-6.00 | 0.060 | 4% | 2.0 |
| 6.00-12.70 | 5% | 2.0 | |
Toleransi panjang: Toleransi panjang untuk panjang helaian sehingga 1000mm maksimum +5/-0 mm.
Kerataan: maks.4% (prosedur mengukur berdasarkan ASTM B708)
Ketumpatan: ≥16.6g/cm³
Kekerasan Vicker: Ketebalan≥0.15mm : ≤125HV
Ujian tegangan:
| Ketebalan(mm) | Kekuatan TeganganMin. (MPa) | 0.2% Kekuatan hasilMin.(MPa) | PemanjanganMin.(%) |
| 0.10-0.15 | 250 | 180 | 15 |
| 0.15-1.50 | 230 | 160 | 20 |
| 1.50-12.70 | 225 | 140 | 30 |
Rupa:Bahan akan berkualiti seragam, bebas daripada bendasing, pecahan dan keretakan. Cadar (tidak dipangkas) mungkin mempunyai rekahan kecil di tepi.