| Molybdenum | Tungsten | Tatanlum | Niobium | I-Chromium |
Ubunzima (20℃) | Uncedo loxinzelelo luyathintelwa:> 220 (HV10) yenziwe ngokutsha>160 – 180[HV10] | isiqabu soxinzelelo luvaliwe:>460(HV30) yenziwe ngokutsha (360 (HV30) | isiphene: 120 – 220 [HV10] yenziwe ngokutsha:80 – 125[HV10] | ikhubazeke: 110 – 180 [HV10] yenziwe ngokutsha: 60 – 110[HV10] | 180 – 250 [HV10] |
Imodyuli yokuqina (20℃) | 320 [GPA] | 405 [GPA] | 186 [GPA] | 104 [GPA] | 294 [GPA] |
I-Coefficient yokwandiswa kwe-thermal yomgama (20℃) | 5.2 · 10-6 [m/(m·K)] | 4.4 · 10-6 [m/(m·K)] | 6.4 · 10-6 [m/(m·K)] | 7.1 · 10-6 [m/(m·K)] | 6.2 · 10-6 [m/(m·K)] |
I-Thermal conductivity (20℃) | 142 [W/(m ·K)] | 164 [W/(m·K)] | 57.5 [W/(m·K)] | 53.7 [W/(m·K)] | 93.7 [W/(m·K)] |
Ubushushu obuthile (20℃) | 0.25 [J/(g·K)] | 0.13 [J/(g·K)] | 0.14 [J/(g·K)] | 0.27 [J/(g·K)] | 0,45 [J/(g·K)] |
Ukuqhutywa koMbane (20℃) | 17.9 · 106 [1/(Ω·m)] | 18.2 · 106 [1/(Ω·m)] | 8 · 106[1/(Ω·m)] | 7.1 · 106[1/(Ω·m)] | 7.9 · 106 [1/(Ω·m)] |
Ukuchasana kombane okuthe ngqo (20℃) | 0,056 [(Ω·mm2)/m] | 0.055 [(Ω·mm2)/m] | 0.125 [(Ω·mm2)/] | 0.141 [(Ω·mm2)/m] | 0.127 [(Ω·mm2)/m] |
Umsebenzi we-electron | 4,39 [eV] | 4.54 [eV] | 4.3 [eV] | 4.3 [eV] | 4,5 [eV] |
Recrystallization ubushushu | 1100℃ | 1350℃ | 900-1450℃ | 850 – 1,300 °C |
|