| Molibden | Volfram | Tatanlum | Niobiy | Chromium |
| Qattiqlik (20 ℃) | Stressni yo'qotish tavlangan:＞ 220（HV10） qayta kristallangan＞160 – 180[HV10] | stressni engillashtiradigan tavlangan:＞460 (HV30) qayta kristallangan＞360（HV30） | deformatsiyalangan: 120 – 220 [HV10] Qayta kristallangan: 80 - 125 [HV10] | deformatsiyalangan: 110 – 180 [HV10] qayta kristallangan: 60 – 110 [HV10] | 180 – 250 [HV10] |
| Elastiklik moduli (20 ℃) | 320 [Gpa] | 405 [Gpa] | 186 [Gpa] | 104 [Gpa] | 294 [Gpa] |
| Chiziqli termal kengayish koeffitsienti (20 ℃) | 5.2 · 10-6 [m/(m·K)] | 4.4 · 10-6 [m/(m·K)] | 6.4 · 10-6 [m/(m·K)] | 7.1 · 10-6 [m/(m·K)] | 6.2 · 10-6 [m/(m·K)] |
| Issiqlik o'tkazuvchanligi (20 ℃) | 142 [Vt/(m ·K)] | 164 [Vt/(m·K)] | 57.5 [Vt/(m·K)] | 53.7 [Vt/(m·K)] | 93.7 [Vt/(m·K)] |
| Maxsus issiqlik (20 ℃) | 0,25 [J/(g·K)] | 0,13 [J/(g·K)] | 0,14 [J/(g·K)] | 0,27 [J/(g·K)] | 0,45 [J/(g·K)] |
| Elektr o'tkazuvchanligi (20 ℃) | 17,9 · 106 [1/(ũ·m)] | 18.2 · 106 [1/(ũ·m)] | 8 · 106[1/(ũ·m)] | 7.1 · 106[1/(ũ·m)] | 7.9 · 106 [1/(ũ·m)] |
| Maxsus elektr qarshiligi (20 ℃) | 0,056 [(O·mm2)/m] | 0,055 [(O·mm2)/m] | 0,125 [(O·mm2)/] | 0,141 [(O·mm2)/m] | 0,127 [(O·mm2)/m] |
| Elektron ish funktsiyasi | 4,39 [eV] | 4,54 [eV] | 4,3 [eV] | 4,3 [eV] | 4,5 [eV] |
| Qayta kristallanish harorat | 1100 ℃ | 1350 ℃ | 900-1450 ℃ | 850 - 1300 ° S gacha |
|
Yuborilgan vaqt: 29-sentyabr, 2019-yil