China TZM Rod. Manufacturer and Supplier

TZM Rod.

Short Description:

Molybdenum-zirconium-titanium rods are a high-performance alloy with molybdenum, zirconium and titanium as the main components. This alloy combines the benefits of all three metals: molybdenum provides strength and stability at high temperatures, zirconium increases corrosion resistance and heat resistance, and titanium increases overall strength and toughness while reducing weight. These properties make molybdenum-zirconium-titanium rods ideal for a wide range of applications in aerospace, nuclear, chemical and high-end manufacturing, particularly in environments requiring extremely high levels of heat and corrosion resistance and mechanical strength. Processing is challenging, but can be achieved with special techniques to meet demanding industry standards.

Send email to us Download as PDF

Product Detail

Product Tags

TZM rods
Chemical composition:

Main and minor components	Min.content(%)	ASTM B386 (361)
Mo	blance	balance
Ti	0.40-0.55%	0.40-0.55%
Zr	0.06-0.12%	0.06-0.12%
Impurities	Max.values (μg/g)	Max.values (μg/g)
Al	10	-
Cu	20	-
Cr	20	-
Fe	20	100
K	20	-
Ni	10	50
Si	20	50
W	300	-
C	100-400	100-400
H	10	-
N	10	20
O	500	300
Cd	5	-
Hg	1	-
Pb	5	-

Dimensions and tolerances:

Diameter (mm)	Diameter tolerance (mm)
Ground
0.50-0.99	±0.007
1.00-1.99	±0.010
1.00-2.99	±0.015
3.00-15.9	±0.020
16.0-24.9	±0.030
25.0-34.9	±0.050
35.0-3939	±0.060
≥40.0	±0.20
Cleaned
0.50-4.0	±2.0%
4.10-10.0	±1.5%
15.0-50.0	±0.30
51.0-75.0	±0.40
75.1-120.0	±1.00
121.0-165.0	±1.50
Turned
40.0-49.9	±0.30
50.0-165.0	±0.40

Length and straightness:

Diameter (mm)	Production length (mm)	Stiraightness/Meter (mm)
Diameter (mm)	Production length (mm)	Cleaned	Ground/turned
0.50-0.99	＞500	＜2.5	＜2.5
1.00-9.90	＞300	＜2.0	＜1.5
10.0-165.0	＞100	＜1.5	＜1.0

Length tolerance:

Diameter 0.50-30.0 mm
Nominal length (mm)	6-30	30-120	120-400	400-1000	1000-2000	＞2000
Length tolerance(mm)	±0.2	±0.3	±0.5	±0.8	±1.2	±2.0
Diameter ＞30.0 mm
Nominal length (mm)	6-30	30-120	120-400	400-1000	1000-2000	＞2000
Length tolerance(mm)	±1.0	±1.5	±2.5	±4.0	±6.0	±8.0

Density:
1. 0.50-40.0 mm ≥10.15g/cm³
2. 40.1-80.0 mm ≥10.10g/cm³
3. 80.1-120.0 mm ≥10.00g/cm³
4. 120.1-165.0 mm ≥9.90g/cm³
Nondestructive testing: For diameters＞15.00 mm:100% ultrasonic testing; For diameters of 0.50-50.0mm:Eddy curent tests on rods with ground.

Diameter(mm)	Tensile strength(MPa)	0.2% Yield Strength(MPa)	Elongation(%)	Hardness(HV 10)
0.50-4.76	-	-	-	-
4.76-22.20	≥790	≥690	≥18
22.20-28.60	≥760	≥655	≥15	260-320
28.60-47.60	≥690	≥585	≥10	250-310
47.60-73.00	≥620	≥550	≥10	245-300
73.00-120.9	≥585	≥515	≥5	240-290
121.0-165	≥585	≥515	≥5	220-280

Surface condition:

Surface：	Cleaned	Ground	Turned
	φ0.50-165mm	φ0.50-50.00mm	φ≥40.00mm
Roughness	Diameter (mm)	Ra (μm) Ground	Ra (μm) Turned
	≤2.50	≤0.80	-
	2.5-50.0	≤1.00	-
	≥40.0	-	≤3.2