Sahani ya Tungsten
Muundo wa kemikali:
| Vipengele kuu na vidogo | Min.maudhui(%) | ASTM B760 |
| W | 99.97 | usawa |
| Uchafu | Thamani za juu (μg/g) | Thamani za juu (μg/g) |
| Al | 15 | - |
| Cu | 10 | - |
| Cr | 20 | - |
| Fe | 30 | 100 |
| K | 10 | - |
| Ni | 20 | 100 |
| Si | 20 | 100 |
| Mo | 300 | - |
| C | 30 | 100 |
| H | 5 | - |
| N | 5 | 100 |
| O | 20 | 100 |
| Cd | 5 | - |
| Hg | 1 | - |
| Pb | 5 | - |
Vipimo na uvumilivu:
Karatasi zilizovingirwa baridi
| Unene(mm) | Uvumilivu wa unene(±mm) | ||
| Upana≤200mm | Upana wa juu 510mm | Uvumilivu wa upana(±mm) | |
| 0.025 | 0.003 | ||
| 0.025-0.03 | 0.004 | 0.5 | |
| 0.03-0.04 | 0.005 | 0.5 | |
| 0.04-0.05 | 0.006 | 0.5 | |
| 0.05-0.06 | 0.008 | 0.5 | |
| 0.06-0.08 | 0.010 | 0.5 | |
| 0.08-0.10 | 0.015 | 0.5 | |
| 0.10-0.15 | 0.025 | 0.045 | 0.5 |
| 0.15-0.30 | 0.035 | 0.060 | 1.0 |
| 0.30-0.40 | 0.05 | 0.085 | 1.6 |
| 0.40-0.50 | 0.06 | 0.110 | 1.6 |
Karatasi zilizochomwa moto
| Unene(mm) | Uvumilivu wa unene(±mm) | ||
| Upana≤510mm | Upana wa juu 1200(mm) | Uvumilivu wa upana(±mm) | |
| 0.05-0.60 | 0.110 | 1.6 | |
| 0.60-0.80 | 0.140 | 2.0 | |
| 0.08-1.00 | 0.200 | 2.0 | |
| 1.00-2.00 | 0.250 | 2.0 | |
| 2.00-8.00 | 0.300 | 2.0 | |
| 8.0-20.00 | 5% | 5% | 2.0 |
Uvumilivu wa urefu: uvumilivu wa urefu kwa vipimo vyote ni upeo +5/-0 mm.
Utulivu: max. 4% (utaratibu wa kupima kwa misingi ya ASTM B760)
Uzito: unene＜10.00mm wiani＞19.2g/cm³
unene (10.00-20.00mm) wiani = 19.1g/cm³
Ugumu wa Vickers:
≤0.10 mm ≥550 HV
0.10-0.05 mm ≥500 HV
0.50-1.50mm ≥470 HV
1.50-10.00mm ≥450 HV
10.00-20.00mm ≥420 HV
Kuonekana: Nyenzo zitakuwa za ubora wa sare, bila ya mambo ya kigeni, mgawanyiko na fractures.
Karatasi ya kitanda (haijapunguzwa) inaweza kuwa na nyufa ndogo za makali.
Ubora wa uso:
Baridi iliyovingirwa ≤ 0.30mm kung'aa
Baridi iliyovingirwa 0.3-0.5 mm iliyochujwa
Imevingirwa moto ≥0.50 mm iliyochujwa