| Molybdenum | Tungsten | Tatanlum | Niobium | Kromium |
| Teu karasa (20 ℃) | Stress-relief annealed:＞ 220 (HV10) rekristalisasi> 160 - 180 [HV10] | stress-relief annealed:> 460 (HV30) rekristalisasi> 360 (HV30) | cacad: 120 – 220 [HV10] rekristalisasi: 80 – 125[HV10] | cacad: 110 - 180 [HV10] rekristalisasi: 60 - 110 [HV10] | 180 – 250 [HV10] |
| Modulus élastisitas (20 ℃) | 320 [GPa] | 405 [GPa] | 186 [GPa] | 104 [GPa] | 294 [GPa] |
| Koéfisién ékspansi termal liniér (20 ℃) | 5.2 · 10-6 [m/(m·K)] | 4.4 · 10-6 [m/(m·K)] | 6.4 · 10-6 [m/(m·K)] | 7.1 · 10-6 [m/(m·K)] | 6.2 · 10-6 [m/(m·K)] |
| konduktivitas termal (20 ℃) | 142 [W/(m ·K)] | 164 [W/(m·K)] | 57.5 [W/(m·K)] | 53.7 [W/(m·K)] | 93.7 [W/(m·K)] |
| Panas spésifik (20 ℃) | 0.25 [J/(g·K)] | 0.13 [J/(g·K)] | 0.14 [J/(g·K)] | 0.27 [J/(g·K)] | 0,45 [J/(g·K)] |
| konduktivitas listrik (20 ℃) | 17.9 · 106 [1/(Ω·m)] | 18.2 · 106 [1/(Ω·m)] | 8 · 106[1/(Ω·m)] | 7.1 · 106[1/(Ω·m)] | 7.9 · 106 [1/(Ω·m)] |
| Résistansi listrik spésifik (20 ℃) | 0,056 [(Ω·mm2)/m] | 0,055 [(Ω·mm2)/m] | 0.125 [(Ω·mm2)/] | 0.141 [(Ω·mm2)/m] | 0.127 [(Ω·mm2)/m] |
| Fungsi gawé éléktron | 4,39 [eV] | 4.54 [eV] | 4.3 [eV] | 4.3 [eV] | 4,5 [eV] |
| Rekristalisasi suhu | 1100 ℃ | 1350 ℃ | 900-1450 ℃ | 850 – 1.300 °C |
|