Heerkulka recrystalization eelanthanum-doped silig molybdenumwuu ka sarreeyaasilig molybdenum saafi ah, waana sababta oo ah qadar yar oo La2O3 ah ayaa hagaajin kara sifooyinka iyo qaab-dhismeedka siliga molybdenum. Ka sokow, saamaynta wajiga labaad ee La2O3 sidoo kale kordhin kartaa xoogga heerkulka qolka eesilig molybdenumiyo hagaajinta heerkulka qolka ka dib dib-u-crystalization.

Isbarbardhigga Heerkulka Dib-u-Crystallization: Qaab-dhismeedka yar-yar ee siliga molybdenum-ka saafiga ah ayaa si cad loo ballaariyay 900 ℃ waxaana dib loo celiyay 1000 ℃. Marka uu kordho heerkulka xuubka, miraha recrystallization ayaa sidoo kale kor u kaca, iyo unugyadu si weyn u yareeyaan. Marka heerkulku gaadho 1200 ℃, siligga molybdenum gabi ahaanba dib ayaa loo celiyay, qaab-dhismeedkiisuna waxa uu muujinayaa mid isku mid ah oo isku siman oo dib ukrastallized ah. Marka heerkulku kordho, hadhuudhku si aan sinnayn ayuu u korayaa wuxuuna u muuqdaa midho qallafsan. Marka la tirtiro 1500 ℃, siliga molybdenum waa sahlan tahay in la jebiyo, qaabdhismeedkeeduna wuxuu muujinayaa hadhuudh siman oo siman. Qaab dhismeedka fiber-ka ee siliga molybdenum-ka lanthanum-doped lanthanum wuu balaaray ka dib markii la tirtiray 1300 ℃, iyo qaabka iligga oo kale ayaa ka soo muuqday xadka fiber-ka. Markay ahayd 1400 ℃, miraha recystallized ayaa soo muuqday. Marka la joogo 1500 ℃, texture fiber-ka ayaa si aad ah hoos ugu dhacay, iyo qaab-dhismeedka dib loo soo celiyay ayaa si cad u muuqday, iyo miraha ayaa u koray si aan sinnayn. Heerkulka dib-u-kicinta ee fiilada molybdenum-ka ee lanthanum-doped ayaa ka sarreeya kan siliga molybdenum-ka saafiga ah, taas oo inta badan ay sabab u tahay saameynta qaybaha wajiga labaad ee La2O3. Wajiga labaad ee La2O3 waxa uu hor istaagaa socdaalka soohdinta hadhuudhka iyo korriinka hadhuudhka, sidaas awgeed waxay kordhinaysaa heerkulka recrystalization.

Isbarbardhigga Guryaha Makaanikada Heerkulka Qolka: Kordhinta siligga molybdenum saafiga ah waxay kordhisaa heerkul-ku-jilicsan oo sii kordhaya. Marka heerkulka anneal at 1200 ℃, elongation gaaro qiimaha ugu badan. Kordhinta ayaa hoos u dhigta heerkulka anneal ee sii kordhaya. Waxaa lagu xiray 1500 ℃, dhererkeeduna wuxuu ku dhow yahay eber. Kordhinta fiilada molybdenum-ka ee La-doped waxay la mid tahay siligga molybdenum saafi ah, iyo heerka dhererkiisu wuxuu gaaraa ugu badnaan marka la tirtiro 1200 ℃. Ka dibna dhererka ayaa hoos u dhacaya heerkulka sii kordhaya. Waxa kaliya ee ka duwan waa heerka dhimista oo gaabis ah. Inkasta oo fidinta molybdenum-ka lanthanum-doped lanthanum uu hoos u dhacay ka dib markii la tirtiray 1200 ℃, dhererku wuu ka sarreeyaa siliga molybdenum saafi ah.