Plat Tungsten
Komposisi kimia:
| Komponen utama dan kecil | kandungan min(%) | ASTM B760 |
| W | 99.97 | imbangan |
| kekotoran | Nilai maks (μg/g) | Nilai maks (μg/g) |
| Al | 15 | - |
| Cu | 10 | - |
| Cr | 20 | - |
| Fe | 30 | 100 |
| K | 10 | - |
| Ni | 20 | 100 |
| Si | 20 | 100 |
| Mo | 300 | - |
| C | 30 | 100 |
| H | 5 | - |
| N | 5 | 100 |
| O | 20 | 100 |
| Cd | 5 | - |
| Hg | 1 | - |
| Pb | 5 | - |
Dimensi dan toleransi:
Cadar canai sejuk
| Ketebalan (mm) | Toleransi ketebalan (± mm) | ||
| Lebar≤200mm | Lebar maksimum 510mm | Toleransi lebar(±mm) | |
| 0.025 | 0.003 | ||
| 0.025-0.03 | 0.004 | 0.5 | |
| 0.03-0.04 | 0.005 | 0.5 | |
| 0.04-0.05 | 0.006 | 0.5 | |
| 0.05-0.06 | 0.008 | 0.5 | |
| 0.06-0.08 | 0.010 | 0.5 | |
| 0.08-0.10 | 0.015 | 0.5 | |
| 0.10-0.15 | 0.025 | 0.045 | 0.5 |
| 0.15-0.30 | 0.035 | 0.060 | 1.0 |
| 0.30-0.40 | 0.05 | 0.085 | 1.6 |
| 0.40-0.50 | 0.06 | 0.110 | 1.6 |
Cadar bergulung panas
| Ketebalan (mm) | Toleransi ketebalan (± mm) | ||
| Lebar≤510mm | Lebar maksimum 1200(mm) | Toleransi lebar(±mm) | |
| 0.05-0.60 | 0.110 | 1.6 | |
| 0.60-0.80 | 0.140 | 2.0 | |
| 0.08-1.00 | 0.200 | 2.0 | |
| 1.00-2.00 | 0.250 | 2.0 | |
| 2.00-8.00 | 0.300 | 2.0 | |
| 8.0-20.00 | 5% | 5% | 2.0 |
Toleransi panjang: toleransi panjang untuk semua dimensi adalah maksimum +5/-0 mm.
Kerataan: maks. 4% (prosedur mengukur berdasarkan ASTM B760)
Ketumpatan: ketebalan ＜10.00mm ketumpatan＞19.2g/cm³
ketebalan（10.00-20.00mm）ketumpatan＞19.1g/cm³
Kekerasan Vickers:
≤0.10 mm ≥550 HV
0.10-0.05 mm ≥500 HV
0.50-1.50mm ≥470 HV
1.50-10.00mm ≥450 HV
10.00-20.00mm ≥420 HV
Penampilan: Bahan akan berkualiti seragam, bebas daripada bendasing, pecahan dan patah.
Cadar (tidak dipangkas) mungkin mempunyai rekahan kecil di tepi.
Kualiti permukaan:
Canai sejuk ≤ 0.30mm terang
Cold rolled 0.3-0.5 mm jeruk
Digulung panas ≥0.50 mm jeruk