Parameter Commom Molibdenum Tungsten Tatanlum Niobium

Molibdenum

Tungsten

Tatanlum

Niobium

Chromium

Kekerasan(20℃)

Anil untuk melegakan tekanan:>

220(HV10)

dihablur semula>160 – 180[HV10]

pelega tekanan annealed:>460(HV30)

dihablur semula>360(HV30)

cacat:120 – 220 [HV10]

dihablur semula:80 – 125[HV10]

cacat:110 – 180 [HV10] terhablur semula:60 – 110[HV10]

180 – 250 [HV10]

Modulus keanjalan(20℃)

320 [GPa]

405 [GPa]

186 [GPa]

104 [GPa]

294 [GPa]

Pekali pengembangan haba linear(20℃)

5.2 · 10-6

[m/(m·K)]

4.4 · 10-6

[m/(m·K)]

6.4 · 10-6

[m/(m·K)]

7.1 · 10-6

[m/(m·K)]

6.2 · 10-6

[m/(m·K)]

Kekonduksian terma(20℃)

142 [W/(m ·K)]

164

[W/(m·K)]

57.5

[W/(m·K)]

53.7

[W/(m·K)]

93.7

[W/(m·K)]

Haba tentu(20℃)

0.25

[J/(g·K)]

0.13

[J/(g·K)]

0.14 [J/(g·K)]

0.27

[J/(g·K)]

0,45

[J/(g·K)]

Kekonduksian elektrik(20℃)

17.9 · 106

[1/(Ω·m)]

18.2 · 106

[1/(Ω·m)]

8 · 106[1/(Ω·m)]

7.1 · 106[1/(Ω·m)]

7.9 · 106

[1/(Ω·m)]

Rintangan elektrik tertentu(20℃)

0,056

[(Ω·mm2)/m]

0.055

[(Ω·mm2)/m]

0.125

[(Ω·mm2)/]

0.141

[(Ω·mm2)/m]

0.127

[(Ω·mm2)/m]

Fungsi kerja elektron

4,39 [eV]

4.54 [eV]

4.3 [eV]

4.3 [eV]

4.5 [eV]

Penghabluran semula

suhu

1100 ℃

1350 ℃

900-1450 ℃

850 – 1,300 °C