Molybdenum Copper Alloy.
Hanganga matū:
| Nga waahanga matua me nga waahanga iti | Min.ihirangi(%) |
| Mo | 67-73 |
| Cu | 27-33 |
| Nga poke | Ngā uara mōrahi (μg/g) |
| Al | 10 |
| Cr | 20 |
| Fe | 20 |
| K | 20 |
| Ni | 10 |
| Si | 30 |
| W | 300 |
| C | 100 |
| H | 10 |
| N | 10 |
| O | 1000 |
| Sn | 10 |
| Sb | 20 |
| Sr | 10 |
| V | 10 |
| Cd | 5 |
| Hg | 1 |
| Pb | 5 |
Te Matotoru me te whanui te whakaarata:
| Whakaaetanga me te whanui | Whakaaetanga whanui | |
| Te matotoru(mm) | Max.400 mm± mm ranei % o te matotoru | [± mm] |
| 0.20-0.30 | 0.020 | 0.5 |
| 0.30-0.40 | 0.030 | 0.5 |
| 0.40-0.60 | 0.035 | 1.6 |
| 0.60-1.00 | 0.040 | 1.6 |
| 1.00-1.50 | 4% | 1.6 |
| 1.50-2.00 | 4% | 1.6 |
Te manawanui
Ko te roa o te roa mo nga rahi katoa ko te teitei +5/-0 mm.
| Papatahi | mōrahi.4% (te tikanga ine i runga i te ASTM B386) |
| Kiato | ≥9,7 g/cm³ |
| Te whakarea roha wera | ≤ 9,5 [10-6 × K-1 ] |
| Ko te kawe werawera [λ i te 20°C] | 150 – 190 [W/mK] |
| Te ātete hiko motuhake [ρ i te 20°C] | ≤ 0,040 [µΩm] |
| [E-Modulus i te 20°C] | 215 - 240 GPa |
| Vickers pakeke | ≥ 180 HV |
| Te ahua | Ka rite te kounga o nga rawa, karekau mai i nga mea kee, nga wehenga me nga pakaru.Ko nga pepa moenga (kaore i whakapaia) ka iti pea nga kapiti taha. |
| Te taratara o te mata | Huri makariri, papa:Ra≤1.5µm |
| Huri makariri: Ra≤1.5µm |