Tantal Rod
Konpozisyon chimik:
| Konpozan prensipal ak minè | Min.content (%) | ASTM B365 |
| Ta | 99.95 | balans |
| Enpurte | Max.values (μg/g) | Max.values (μg/g) |
| Fe | 100 | 100 |
| Mo | 100 | 200 |
| Nb | 400 | 1000 |
| Ni | 50 | 100 |
| Si | 50 | 50 |
| Ti | 50 | 100 |
| W | 100 | 500 |
| C | 30 | 200 |
| H | 15 | 15 |
| N | 50 | 100 |
| O | 100 | 250 |
| Cd | 10 | - |
| Hg | 1 | - |
| Pb | 10 | - |
Dyamèt ak tolerans
| Dyamèt (mm) | Tolerans dyamèt (mm) |
| Tè | |
| 3.00-15.9 | ±0.05 |
| 16.0-24.9 | ± 0.10 |
| 25.0-34.9 | ± 0.25 |
| 35.0-39.9 | ±0.40 |
| 40.0-50.0 | ±0.80 |
| Netwaye | |
| 3.00-4.74 | ±0.076 |
| 4.75-9.51 | ± 0.102 |
| 9.52-12.69 | ± 0.127 |
| 12.70-15.87 | ±0.178 |
| 15.88-19.04 | ±0.203 |
| 19.05-25.39 | ±0.254 |
| 25.40-38.09 | ± 0.381 |
| 38.10-50.79 | ±0.508 |
| 50.80-63.49 | ±0.762 |
| 63.50-120.0 | ± 1.50 |
| Vire | |
| 30.0-49.9 | ± 0.30 |
| 50.0-120.0 | ±0.40 |
Longè ak dwat:
| Dyamèt (mm) | Longè pwodiksyon (mm) | Dwazite/Mèt (mm) | |
| Netwaye | Atè/vire | ||
| 3.00-9.90 | >500 | ＜2.5 | ＜2.0 |
| 10.0-120.0 | >300 | ＜2.5 | ＜1.5 |
Tolerans longè:
| Longè nominal (mm) | 6-30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | > 2000 |
| Tolerans longè (mm) | ± 1.0 | ±1.5 | ± 2.5 | ± 4.0 | ± 6.0 | ± 8.0 |
Dansite: ≥16.6g/cm³
Tès nondestructive: Pou dyamèt > 15.00 mm: 100% tès ultrasons; Pou dyamèt 0.50-50.0mm: Eddy aktyèl tès sou branch bwa ak sifas tè.
| Dyamèt (mm) | Fòs rupture(MPa) | 0.2% SedeFòs(MPa) | Elongasyon(%) |
| 3.00-3.19 | ≥207 | - | ≥20 |
| 3.20-63.5 | ≥172 | ≥103 | ≥25 |
Kondisyon sifas:
| Sifas | marinated | Tè | Vire |
| φ3.0-165.0mm | φ3.0-50.00mm | φ≥30.00mm | |
| Brutalizasyon | Dyamèt (mm) | Ra (μm) Tè | Ra (μm) Vire |
| 3.0-50.0 | ≤1.20 | - | |
| ≥30.0 | - | ≤3.2 |