Paramèt komen nan Molybdenum Tungstène Tatanlum Niobium

Molybdène

Tengstèn

Tatanlum

Niobyòm

Kwòm

Dite (20 ℃)

Estrès-soulajman annealed:>

220(HV10)

rekristalize>160 - 180[HV10]

soulajman estrès rkwit:> 460 (HV30)

rekristalize>360(HV30)

defòme: 120 - 220 [HV10]

rekristalize: 80 - 125 [HV10]

defòme: 110 - 180 [HV10] rekristalize: 60 - 110 [HV10]

180 – 250 [HV10]

Modil elastisite (20 ℃)

320 [GPa]

405 [GPa]

186 [GPa]

104 [GPa]

294 [GPa]

Koefisyan ekspansyon tèmik lineyè (20 ℃)

5.2 · 10-6

[m/(m·K)]

4.4 · 10-6

[m/(m·K)]

6.4 · 10-6

[m/(m·K)]

7.1 · 10-6

[m/(m·K)]

6.2 · 10-6

[m/(m·K)]

Konduktivite tèmik (20 ℃)

142 [W/(m ·K)]

164

[W/(m·K)]

57.5

[W/(m·K)]

53.7

[W/(m·K)]

93.7

[W/(m·K)]

Chalè espesifik (20 ℃)

0.25

[J/(g·K)]

0.13

[J/(g·K)]

0.14 [J/(g·K)]

0.27

[J/(g·K)]

0,45

[J/(g·K)]

Konduktivite elektrik (20 ℃)

17.9 · 106

[1/(Ω·m)]

18.2 · 106

[1/(Ω·m)]

8 · 106[1/(Ω·m)]

7.1 · 106[1/(Ω·m)]

7.9 · 106

[1/(Ω·m)]

Rezistans elektrik espesifik (20 ℃)

0,056

[(Ω·mm2)/m]

0.055

[(Ω·mm2)/m]

0.125

[(Ω·mm2)/]

0.141

[(Ω·mm2)/m]

0.127

[(Ω·mm2)/m]

Fonksyon travay elèktron

4,39 [eV]

4.54 [eV]

4.3 [eV]

4.3 [eV]

4,5 [eV]

Rekristalizasyon

tanperati

1100℃

1350℃

900-1450 ℃

850 - 1,300 °C


Tan pòs: 29 septanm 2019