Hot-selling China 1800 Hot Bent High Quality Mosi2 Heating Element, U Type Molybdenum Disilicide Rod
We enjoy a very good reputation among our customers for our excellent product quality, competitive price and the best service for Hot-selling China 1800 Hot Bent High Quality Mosi2 Heating Element, U Type Molybdenum Disilicide Rod, Leading the trend of this field is our persistent objective. Supplying first class solutions is our intention. To create a beautiful upcoming, we wish to cooperate with all close friends in the home and overseas. Should you have got any interest in our products and solutions, remember to never wait to call us.
We enjoy a very good reputation among our customers for our excellent product quality, competitive price and the best service for 1800 Mosi2 Heating Elements, China Heating Elements, We integrate all our advantages to continuously innovate, improve and optimize our industrial structure and product performance. We are going to always believe in and work on it. Welcome to join us to promote green light, together we will make a better Future!
Molybdenum rods Chemical composition:
| Main and minor components | Min.content(%) | ASTM B386 (361) |
| Mo | 99.95 | balance |
| Impurities | Max.values (μg/g) | Max.values (μg/g) |
| Al | 10 | - |
| Cu | 20 | - |
| Cr | 20 | - |
| Fe | 20 | 100 |
| K | 20 | - |
| Ni | 10 | 50 |
| Si | 20 | 100 |
| W | 300 | - |
| C | 30 | 100 |
| H | 10 | 20 |
| N | 10 | 70 |
| O | 40 | - |
| Cd | 5 | - |
| Hg | 1 | - |
| Pb | 5 | - |
Dimensions and tolerances:
| Diameter (mm) | Diameter tolerance (mm) |
| Ground | |
| 0.50-0.99 | ±0.007 |
| 1.00-1.99 | ±0.010 |
| 1.00-2.99 | ±0.015 |
| 3.00-15.9 | ±0.020 |
| 16.0-24.9 | ±0.030 |
| 25.0-34.9 | ±0.050 |
| 35.0-3939 | ±0.060 |
| ≥40.0 | ±0.20 |
| Cleaned | |
| 0.50-4.0 | ±2.0% |
| 4.10-10.0 | ±1.5% |
| 15.0-50.0 | ±0.30 |
| 51.0-75.0 | ±0.40 |
| 75.1-120.0 | ±1.00 |
| 121.0-165.0 | ±1.50 |
| Turned | |
| 40.0-49.9 | ±0.30 |
| 50.0-165.0 | ±0.40 |
Length and straightness:
| Diameter (mm) | Production length (mm) | Stiraightness/Meter (mm) | |
| Cleaned | Ground/turned | ||
| 0.50-0.99 | ＞500 | ＜2.5 | ＜2.5 |
| 1.00-9.90 | ＞300 | ＜2.0 | ＜1.5 |
| 10.0-165.0 | ＞100 | ＜1.5 | ＜1.0 |
Length tolerance:
| Diameter 0.50-30.0 mm | ||||||
| Nominal length (mm) | 6-30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | ＞2000 |
| Length tolerance(mm) | ±0.2 | ±0.3 | ±0.5 | ±0.8 | ±1.2 | ±2.0 |
| Diameter ＞30.0 mm | ||||||
| Nominal length (mm) | 6-30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | ＞2000 |
| Length tolerance(mm) | ±1.0 | ±1.5 | ±2.5 | ±4.0 | ±6.0 | ±8.0 |
Density:
1. 00.50-40.0 mm ≥10.15g/cm³
2. 40.1-80.0 mm ≥10.10g/cm³
3. 80.1-120.0 mm ≥10.00g/cm³
4. 120.1-165.0 mm ≥9.90g/cm³
Nondestructive testing: For diameters＞15.00 mm:100% ultrasonic testing; For diameters of 0.50-50.0mm:Eddy curent tests on rods with ground surface.
| Diameter(mm) | Tensile strength(MPa) | 0.2% Yield Strength(MPa) | Elongation(%) | Hardness(HV 10) |
| 0.50-3.18 | ≥585 | ≥450 | ≥15 | |
| 3.18-10.30 | ≥515 | ≥380 | ≥15 | |
| 10.32-22.20 | ≥620 | ≥515 | ≥18 | 230-280 |
| 22.20-28.60 | ≥585 | ≥480 | ≥15 | 225-270 |
| 28.60-47.60 | ≥515 | ≥450 | ≥10 | 215-260 |
| 47.60-73.00 | ≥480 | ≥415 | ≥10 | 210-250 |
| 73.00-88.90 | ≥450 | ≥380 | ≥10 | 205-240 |
| 89.00-120.9 | ≥450 | ≥380 | ≥5 | 200-240 |
| 121.0-164.9 | ≥450 | ≥380 | ≥5 | 180-240 |
| 165.0 | ≥450 | ≥380 | ≥- | 180-240 |
Surface condition:
| Surface： | Cleaned | Ground | Turned |
| φ0.50-165mm | φ0.50-50.00mm | φ≥40.00mm | |
| Roughness | Diameter (mm) | Ra (μm) Ground | Ra (μm) Turned |
| ≤2.50 | ≤0.80 | - | |
| 2.5-50.0 | ≤1.00 | - | |
| ≥40.0 | - | ≤3.2 |