Commom Parameter na Molybdenum Tungsten Tatanlum Niobium

Molybdenum

Tungsten

Tatanlum

Niobium

Chromium

Hardness (20 ℃)

An warware matsalar damuwa: :

220 (HV10)

recrystallized: 160-180[HV10]

Taimakon damuwa: >460(HV30)

recrystallized: 360 (HV30)

nakasassu: 120-220 [HV10]

recrystallized: 80-125[HV10]

nakasassu: 110 - 180 [HV10] recrystallized: 60 - 110[HV10]

180-250 [HV10]

Modulus na elasticity (20 ℃)

320 [GPa]

405 [GPa]

186 [GPa]

104 [GPa]

294 [GPa]

Coefficient na linzamin kwamfuta fadada thermal (20 ℃)

5.2 · 10-6

[m/ (m·K)]

4.4 · 10-6

[m/ (m·K)]

6.4 · 10-6

[m/ (m·K)]

7.1 · 10-6

[m/ (m·K)]

6.2 · 10-6

[m/ (m·K)]

Thermal conductivity (20 ℃)

142 [W/ (m · K)]

164

[W/ (m·K)]

57.5

[W/ (m·K)]

53.7

[W/ (m·K)]

93.7

[W/ (m·K)]

Musamman zafi (20 ℃)

0.25

[J/ (g·K)]

0.13

[J/ (g·K)]

0.14 [J/ (g·K)]

0.27

[J/ (g·K)]

0,45

[J/ (g·K)]

Wutar lantarki (20 ℃)

17.9 · 106

[1/ (Ω·m)]

18.2 · 106

[1/ (Ω·m)]

8 · 106[1/ (Ω·m)]

7.1 · 106[1/ (Ω·m)]

7.9 · 106

[1/ (Ω·m)]

Musamman juriya na lantarki (20 ℃)

0,056

[(Ω·mm2)/m]

0.055

[(Ω·mm2)/m]

0.125

[(Ω·mm2)/]

0.141

[(Ω·mm2)/m]

0.127

[(Ω·mm2)/m]

Electron aiki aiki

4,39 [eV]

4.54 [eV]

4.3 [eV]

4.3 [eV]

4,5 [eV]

Recrystallization

zafin jiki

1100 ℃

1350 ℃

900-1450 ℃

850 - 1,300 °C


Lokacin aikawa: Satumba-29-2019