Good quality Niobium Bar Rod - Molybdenum Sheet – Forged Tungsten
Good quality Niobium Bar Rod - Molybdenum Sheet – Forged Tungsten Detail:
Molybdenum Sheet
1.Thickness and width tolerances
Cold rolled sheets
| Thickness(mm) | Thickness tolerance(±mm) | Max.width(mm) | Width tolerance(±mm) |
| 0.10 | 0.008 | 305 | 0.5 |
| 0.10-0.127 | 0.010 | 305 | 0.5 |
| 0.127-0.15 | 0.010 | 610 | 0.5 |
| 0.15-0.25 | 0.015 | 800 | 0.5 |
| 0.25-0.50 | 0.020 | 915 | 1.6 |
| 0.50-0.80 | 0.028 | 915 | 1.6 |
| 0.80-1.20 | 0.035 | 915 | 1.6 |
| 1.20-2.00 | 3% | 915 | 1.6 |
Cold rooled sheets
| Thickness(mm) | Thickness tolerance(±mm) | Max.width(mm) | Width tolerance(±mm) |
| 1.00 | 0.080 | 850 | 2.0 |
| 1.00-1.50 | 0.130 | 850 | 2.0 |
| 1.50-2.00 | 0.150 | 850 | 2.0 |
| 2.00-3.60 | 0.180 | 1200 | 2.0 |
| 3.60-50.00 | 5% | 1500 | 2.0 |
Length tolerace:
The length tolerace for sheet length up to 2500 mm is max. +5/-0 mm.
The length tolerance of sheet cuts can vary with a total tolerance range not exceeding the above given value. The maximum sheet dimensions depend on the sheet thickness.other dimensions upon request.
Sheet with premium surface condition are available from 0.15 to 1 mm.Sheet with thickness from 0.127 to 0.381 mm can be delivered as coils upon request.(production length max.10500mm)
Flatness:
Max.1% for sheet thickness≥0.3mm
Max.4% for sheet thickness＜0.3mm
(measuring proedure on the basis of ASTM B386)
2. Physical and mechanical product properties.
Density: ≥10.2g/cm³
Vickers Hardness:
≤1.0mm: 240-280 HV
1.00-3.60mm: 240-270 HV
306-10.00mm: 220-270 HV
10.00-50.00: ＞200 HV
Tensile test:
| Thickness(mm) | Tensile Srenght Min. (MPa) | 0.2 % Yield strength Min. (MPa) | ElongationMin.(%) |
| 0.1-0.25 | 700 | 620 | 2.0 |
| 0.25-0.40 | 680 | 590 | 3.0 |
| 0.40-0.65 | 680 | 590 | 5.0 |
| 0.65-1.50 | 680 | 580 | 10.0 |
| 1.50-2.30 | 640 | 580 | 12.0 |
| 2.30-5.00 | 640 | 580 | 15.0 |
| 5.00-10.00 | 640 | 580 | 10.0 |
| 10.00-13.00 | 590 | 540 | 10.0 |
| 13.00-25.00 | 500 | 480 | 2.0 |
| 25.00-50.00 | 500 | 480 | 1.0 |
Surface condition
Appearance: The material will be of uniform quality, free from foreign matter, splits and fractures. bed sheet(not trimmed) may have small edge cracks.
Surface defects are assessed in the frame of visual inspection.
Local surface defects can be removed by frinding within the specified thickness tolerace.
Surface condition: Cold rolled, bright(≤1mm) Ra≤0.20μm
Cold rolled, pickled: Ra≤1.00μm
Cold rolled ground: Ra≤0.60μm
Chemical composition:
| Main and minor components | Min.content(%) | ASTM B386 (361) |
| Mo | 99.97 | balance |
| Impurities | Max.values (μg/g) | Max.values (μg/g) |
| Al | 10 | - |
| Cu | 20 | - |
| Cr | 20 | - |
| Fe | 20 | 100 |
| K | 20 | - |
| Ni | 10 | 50 |
| Si | 20 | 100 |
| W | 300 | - |
| C | 30 | 100 |
| H | 10 | 20 |
| N | 10 | 70 |
| O | 40 | - |
| Cd | 5 | - |
| Hg | 1 | - |
| Pb | 5 | - |
Product detail pictures:
Related Product Guide:
Molybdenum Products for Furnaces : Quote, RFQ, Price and Buy | Slivery Color Molybdenum Sheet /Plate
Global MoSi2 Heating Element Market Insights Report 2019-2023: Kanthal, I Squared R, Henan Songshan, ZIRCAR, Yantai Torch, MHI | Niobium Carbide Alloy Powder
Persisting in "High quality, Prompt Delivery, Aggressive Price", we have established long-term cooperation with clientele from both equally overseas and domestically and get new and old clients' higher comments for Good quality Niobium Bar Rod - Molybdenum Sheet – Forged Tungsten , The product will supply to all over the world, such as: Jordan, Portugal, Johor, The design, processing, purchasing, inspection, storage, assembling process are all in scientific and effective documentary process , increasing usage level and reliability of our brand deeply, which makes us become superior supplier of the four major product categories shell castings domestically and obtained the customer's trust well.
By Ray from Israel - 2017.06.16 18:23
The supplier cooperation attitude is very good, encountered various problems, always willing to cooperate with us, to us as the real God.
By Naomi from Roman - 2017.11.01 17:04