| Molybdenwm | Twngsten | Tatanlum | Niobium | Cromiwm |
| Caledwch （20 ℃） | Rhyddhad straen wedi'i anelio: ＞ 220 （HV10） wedi'i ailgrisialu ＞ 160 – 180[HV10] | rhyddhad straen wedi'i anelio: ＞460(HV30) wedi'i ailgrisialu ＞ 360 （HV30） | wedi'i ddadffurfio: 120 - 220 [HV10] wedi'i ailgrisialu: 80 - 125[HV10] | wedi'i ddadffurfio: 110 - 180 [HV10] wedi'i ailgrisialu: 60 - 110 [HV10] | 180 – 250 [HV10] |
| Modwlws elastigedd （20 ℃） | 320 [GPa] | 405 [GPa] | 186 [GPa] | 104 [GPa] | 294 [GPa] |
| Cyfernod ehangu thermol llinellol （20 ℃） | 5.2·10-6 [m/(m·K)] | 4.4·10-6 [m/(m·K)] | 6.4·10-6 [m/(m·K)] | 7.1·10-6 [m/(m·K)] | 6.2·10-6 [m/(m·K)] |
| Dargludedd thermol （20 ℃） | 142 [C/(m ·K)] | 164 [W/(m·K)] | 57.5 [W/(m·K)] | 53.7 [W/(m·K)] | 93.7 [W/(m·K)] |
| Gwres penodol （20 ℃） | 0.25 [J/(g·K)] | 0.13 [J/(g·K)] | 0.14 [J/(g·K)] | 0.27 [J/(g·K)] | 0,45 [J/(g·K)] |
| Dargludedd trydanol （20 ℃） | 17.9·106 [1/(Ω·m)] | 18.2·106 [1/(Ω·m)] | 8·106[1/(Ω·m)] | 7.1·106[1/(Ω·m)] | 7.9·106 [1/(Ω·m)] |
| Gwrthiant trydanol penodol （20 ℃） | 0,056 [(Ω·mm2)/m] | 0.055 [(Ω·mm2)/m] | 0. 125 [(Ω·mm2)/] | 0. 141 [(Ω·mm2)/m] | 0. 127 [(Ω·mm2)/m] |
| Swyddogaeth gwaith electron | 4,39 [eV] | 4.54 [eV] | 4.3 [eV] | 4.3 [eV] | 4,5 [eV] |
| Ailgrisialu tymheredd | 1100 ℃ | 1350 ℃ | 900-1450 ℃ | 850 – 1,300°C |
|